1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60 61 62 63 64 65 66 67 68 69 70 71 72 73 74 75 76 77 78 79 80 81 82 83 84 85 86 87 88 89 90 91 92 93 94 95 96 97 98 99 100 101 102 103 104 105 106 107 108 109 110 111 112 113 114 115 116 117 118 119 120 121 122 123 124 125 126 127 128 129 130 131 132 133 134 135 136 137 138 139 140 141 142 143 144 145 146 147 148 149 150 151 152 153 154 155 156 157 158 159 160
|
Reactive MD-force field: Fe/O/water: Aryanpour, M.; van Duin, A. C. T.; Kubicki, J. D. J. Phys. Chem. A 2010, 114, 6298-6307
39 ! Number of general parameters
50.0000 !Overcoordination parameter
9.5469 !Overcoordination parameter
1.6725 !Valency angle conjugation parameter
1.7224 !Triple bond stabilisation parameter
6.8702 !Triple bond stabilisation parameter
60.4850 !C2-correction
1.0588 !Undercoordination parameter
4.6000 !Triple bond stabilisation parameter
12.1176 !Undercoordination parameter
13.3056 !Undercoordination parameter
-55.1978 !Triple bond stabilization energy
0.0000 !Lower Taper-radius
10.0000 !Upper Taper-radius
2.8793 !Not used
33.8667 !Valency undercoordination
6.0891 !Valency angle/lone pair parameter
1.0563 !Valency angle
2.0384 !Valency angle parameter
6.1431 !Not used
6.9290 !Double bond/angle parameter
0.3989 !Double bond/angle parameter: overcoord
3.9954 !Double bond/angle parameter: overcoord
-2.4837 !Not used
5.7796 !Torsion/BO parameter
10.0000 !Torsion overcoordination
1.9487 !Torsion overcoordination
-1.2327 !Conjugation 0 (not used)
2.1645 !Conjugation
1.5591 !vdWaals shielding
0.1000 !Cutoff for bond order (*100)
1.7602 !Valency angle conjugation parameter
0.6991 !Overcoordination parameter
50.0000 !Overcoordination parameter
1.8512 !Valency/lone pair parameter
0.5000 !Not used
20.0000 !Not used
5.0000 !Molecular energy (not used)
0.0000 !Molecular energy (not used)
0.7903 !Valency angle conjugation parameter
4 ! Nr of atoms; cov.r; valency;a.m;Rvdw;Evdw;gammaEEM;cov.r2;#
alfa;gammavdW;valency;Eunder;Eover;chiEEM;etaEEM;n.u.
cov r3;Elp;Heat inc.;n.u.;n.u.;n.u.;n.u.
ov/un;val1;n.u.;val3,vval4
C 1.3817 4.0000 12.0000 1.8903 0.1838 0.9000 1.1341 4.0000
9.7559 2.1346 4.0000 34.9350 79.5548 5.9666 7.0000 0.0000
1.2114 0.0000 202.6057 8.9539 34.9289 13.5366 0.8563 0.0000
-2.8983 2.5000 1.0564 4.0000 2.9663 0.0000 0.0000 0.0000
H 0.8930 1.0000 1.0080 1.3550 0.0930 0.8203 -0.1000 1.0000
8.2230 33.2894 1.0000 0.0000 121.1250 3.7248 9.6093 1.0000
-0.1000 0.0000 61.6606 3.0408 2.4197 0.0003 1.0698 0.0000
-19.4571 4.2733 1.0338 1.0000 2.8793 0.0000 0.0000 0.0000
O 1.2450 2.0000 15.9990 2.3890 0.1000 1.0898 1.0548 6.0000
9.7300 13.8449 4.0000 37.5000 116.0768 8.5000 8.3122 2.0000
0.9049 0.4056 59.0626 3.5027 0.7640 0.0021 0.9745 0.0000
-3.5500 2.9000 1.0493 4.0000 2.9225 0.0000 0.0000 0.0000
Fe 1.9506 3.0000 55.8450 2.0308 0.1274 0.7264 -1.0000 3.0000
11.0534 2.2637 3.0000 0.0000 18.3725 1.2457 7.3021 0.0000
-1.2000 0.0000 66.4838 30.0000 1.0000 0.0000 0.8563 0.0000
-16.2040 2.7917 1.0338 6.0000 2.5791 0.0000 0.0000 0.0000
10 ! Nr of bonds; Edis1;LPpen;n.u.;pbe1;pbo5;13corr;pbo6
pbe2;pbo3;pbo4;Etrip;pbo1;pbo2;ovcorr
1 1 158.2004 99.1897 78.0000 -0.7738 -0.4550 1.0000 37.6117 0.4147
0.4590 -0.1000 9.1628 1.0000 -0.0777 6.7268 1.0000 0.0000
1 2 169.4760 0.0000 0.0000 -0.6083 0.0000 1.0000 6.0000 0.7652
5.2290 1.0000 0.0000 1.0000 -0.0500 6.9136 0.0000 0.0000
2 2 153.3934 0.0000 0.0000 -0.4600 0.0000 1.0000 6.0000 0.7300
6.2500 1.0000 0.0000 1.0000 -0.0790 6.0552 0.0000 0.0000
1 3 164.4303 82.6772 60.8077 -0.3739 -0.2351 1.0000 10.5036 1.0000
0.4475 -0.2288 7.0250 1.0000 -0.1363 4.8734 0.0000 0.0000
3 3 142.2858 145.0000 50.8293 0.2506 -0.1000 1.0000 29.7503 0.6051
0.3451 -0.1055 9.0000 1.0000 -0.1225 5.5000 1.0000 0.0000
2 3 160.0000 0.0000 0.0000 -0.5725 0.0000 1.0000 6.0000 0.5626
1.1150 1.0000 0.0000 0.0000 -0.0920 4.2790 0.0000 0.0000
1 4 133.0514 0.0000 0.0000 1.0000 -0.3000 1.0000 36.0000 0.0673
0.2350 -0.3500 15.0000 1.0000 -0.1143 4.5217 1.0000 0.0000
2 4 105.0054 0.0000 0.0000 -0.0717 0.0000 0.0000 6.0000 0.0505
0.1000 1.0000 0.0000 1.0000 -0.1216 4.5062 0.0000 0.0000
3 4 65.7713 0.0000 0.0000 0.1366 -0.3000 1.0000 36.0000 0.0494
0.9495 -0.3500 15.0000 1.0000 -0.0555 7.9897 1.0000 0.0000
4 4 38.7471 0.0000 0.0000 0.3595 -0.2000 0.0000 16.0000 0.2749
1.0000 -0.2000 15.0000 1.0000 -0.0771 6.4477 0.0000 0.0000
6 ! Nr of off-diagonal terms; Ediss;Ro;gamma;rsigma;rpi;rpi2
1 2 0.1239 1.4004 9.8467 1.1210 -1.0000 -1.0000
2 3 0.0283 1.2885 10.9190 0.9215 -1.0000 -1.0000
1 3 0.1345 1.8422 9.7725 1.2835 1.1576 1.0637
1 4 0.1358 1.8293 10.0425 1.6096 -1.0000 -1.0000
2 4 0.0640 1.6974 11.5167 1.3517 -1.0000 -1.0000
3 4 0.0846 1.4284 10.0808 1.8339 -1.0000 -1.0000
37 ! Nr of angles;at1;at2;at3;Thetao,o;ka;kb;pv1;pv2
1 1 1 59.0573 30.7029 0.7606 0.0000 0.7180 6.2933 1.1244
1 1 2 65.7758 14.5234 6.2481 0.0000 0.5665 0.0000 1.6255
2 1 2 70.2607 25.2202 3.7312 0.0000 0.0050 0.0000 2.7500
1 2 2 0.0000 0.0000 6.0000 0.0000 0.0000 0.0000 1.0400
1 2 1 0.0000 3.4110 7.7350 0.0000 0.0000 0.0000 1.0400
2 2 2 0.0000 27.9213 5.8635 0.0000 0.0000 0.0000 1.0400
1 1 3 53.9517 7.8968 2.6122 0.0000 3.0000 58.6562 1.0338
3 1 3 76.9627 44.2852 2.4177 -25.3063 1.6334 -50.0000 2.7392
2 1 3 65.0000 16.3141 5.2730 0.0000 0.4448 0.0000 1.4077
1 3 1 72.6199 42.5510 0.7205 0.0000 2.9294 0.0000 1.3096
1 3 3 81.9029 32.2258 1.7397 0.0000 0.9888 68.1072 1.7777
3 3 3 80.7324 30.4554 0.9953 0.0000 3.0000 50.0000 1.0783
1 3 2 70.1101 13.1217 4.4734 0.0000 0.8433 0.0000 3.0000
2 3 3 75.6935 50.0000 2.0000 0.0000 1.0000 0.0000 1.1680
2 3 2 85.8000 9.8453 2.2720 0.0000 2.8635 0.0000 1.5800
1 2 3 0.0000 25.0000 3.0000 0.0000 1.0000 0.0000 1.0400
3 2 3 0.0000 15.0000 2.8900 0.0000 0.0000 0.0000 2.8774
2 2 3 0.0000 8.5744 3.0000 0.0000 0.0000 0.0000 1.0421
1 4 1 29.1655 3.3035 0.2000 0.0000 1.1221 0.0000 1.0562
1 1 4 59.8697 2.8115 1.9262 0.0000 0.7602 0.0000 1.4056
1 4 4 25.4591 15.9430 0.9664 0.0000 2.2242 0.0000 1.1088
4 1 4 88.6279 26.0015 1.0328 0.0000 0.2361 0.0000 2.0576
2 1 4 47.3695 16.9204 4.1052 0.0000 0.1000 0.0000 1.0050
2 4 2 34.1965 6.6782 6.5943 0.0000 1.3895 0.0000 1.5365
2 2 4 0.1000 30.0000 3.4094 0.0000 2.4379 0.0000 1.5166
4 2 4 0.0000 8.2994 5.7832 0.0000 2.9873 0.0000 1.7716
2 4 4 21.2590 6.5954 0.9951 0.0000 2.8006 0.0000 1.0000
2 4 4 180.0000 -6.9970 24.3956 0.0000 0.7878 0.0000 1.3672
1 3 4 90.0000 12.8684 1.4601 0.0000 0.8757 0.0000 1.0000
3 1 4 18.8567 24.3753 3.9647 0.0000 0.1000 0.0000 1.5314
3 4 3 79.7335 0.0100 0.1392 0.0000 0.4968 0.0000 2.1948
4 3 4 57.6787 4.8566 2.5768 0.0000 0.7552 0.0000 1.0000
2 3 4 59.4556 10.2025 0.7481 0.0000 1.4521 0.0000 1.0000
3 3 4 73.6721 32.6330 1.7223 0.0000 1.0221 0.0000 1.4351
3 4 4 65.7545 5.6268 4.0645 0.0000 1.7794 0.0000 2.6730
3 2 4 0.0000 4.6026 2.5343 0.0000 0.7284 0.0000 1.1051
2 4 3 34.0653 20.1868 4.7461 0.0000 0.1000 0.0000 1.6752
29 ! Nr of torsions;at1;at2;at3;at4;;V1;V2;V3;V2(BO);vconj;n.u;n
1 1 1 1 -0.2500 34.7453 0.0288 -6.3507 -1.6000 0.0000 0.0000
1 1 1 2 -0.2500 29.2131 0.2945 -4.9581 -2.1802 0.0000 0.0000
2 1 1 2 -0.2500 31.2081 0.4539 -4.8923 -2.2677 0.0000 0.0000
1 1 1 3 1.2799 20.7787 -0.5249 -2.5000 -1.0000 0.0000 0.0000
2 1 1 3 1.9159 19.8113 0.7914 -4.6995 -1.0000 0.0000 0.0000
3 1 1 3 -1.4477 16.6853 0.6461 -4.9622 -1.0000 0.0000 0.0000
1 1 3 1 0.4816 19.6316 -0.0057 -2.5000 -1.0000 0.0000 0.0000
1 1 3 2 1.2044 80.0000 -0.3139 -6.1481 -1.0000 0.0000 0.0000
2 1 3 1 -2.5000 31.0191 0.6165 -2.7733 -2.9807 0.0000 0.0000
2 1 3 2 -2.4875 70.8145 0.7582 -4.2274 -3.0000 0.0000 0.0000
1 1 3 3 -0.3566 10.0000 0.0816 -2.6110 -1.9631 0.0000 0.0000
2 1 3 3 -1.4383 80.0000 1.0000 -3.6877 -2.8000 0.0000 0.0000
3 1 3 1 -1.1390 78.0747 -0.0964 -4.5172 -3.0000 0.0000 0.0000
3 1 3 2 -2.5000 70.3345 -1.0000 -5.5315 -3.0000 0.0000 0.0000
3 1 3 3 -2.0234 80.0000 0.1684 -3.1568 -2.6174 0.0000 0.0000
1 3 3 1 1.1637 -17.3637 0.5459 -3.6005 -2.6938 0.0000 0.0000
1 3 3 2 -2.1289 12.8382 1.0000 -5.6657 -2.9759 0.0000 0.0000
2 3 3 2 2.5000 -22.9397 0.6991 -3.3961 -1.0000 0.0000 0.0000
1 3 3 3 2.5000 -25.0000 1.0000 -2.5000 -1.0000 0.0000 0.0000
2 3 3 3 -2.5000 -2.5103 -1.0000 -2.5000 -1.0000 0.0000 0.0000
3 3 3 3 -2.5000 -25.0000 1.0000 -2.5000 -1.0000 0.0000 0.0000
0 1 2 0 0.0000 0.0000 0.0000 0.0000 0.0000 0.0000 0.0000
0 2 2 0 0.0000 0.0000 0.0000 0.0000 0.0000 0.0000 0.0000
0 2 3 0 0.0000 0.1000 0.0200 -2.5415 0.0000 0.0000 0.0000
0 1 1 0 0.0000 50.0000 0.3000 -4.0000 -2.0000 0.0000 0.0000
0 3 3 0 0.5511 25.4150 1.1330 -5.1903 -1.0000 0.0000 0.0000
1 1 3 3 -0.0002 20.1851 0.1601 -9.0000 -2.0000 0.0000 0.0000
1 3 3 1 0.0002 80.0000 -1.5000 -4.4848 -2.0000 0.0000 0.0000
3 1 3 3 -0.1583 20.0000 1.5000 -9.0000 -2.0000 0.0000 0.0000
1 ! Nr of hydrogen bonds;at1;at2;at3;Rhb;Dehb;vhb1
3 2 3 2.1200 -3.5800 1.4500 19.5000
|